Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.40 g/cm³ |
| Apparent density | | | 0.85 g/cm³ |
| Melt volume flow rate | | ISO1133 | 7.50 cm³/10min |
| Shrinkage rate | | ISO294-4 | 2.1 % |
| Shrinkage rate | | ISO294-4 | 2.1 % |
| Water absorption rate | | ISO62 | 0.80 % |
| Water absorption rate | | ISO62 | 0.20 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ISO2039-1 | 130 MPa |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Flammability level | | IEC60695-11-10,-20 | HB |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| ISOType | | ISO9988-1 | POM-K,M-GNR,03-002 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile strain | Yield | ISO527-2/50 | 13 % |
| Nominal tensile fracture strain | | ISO527-2/50 | 33 % |
| Tensile creep modulus | | ISO899-1 | 1000 MPa |
| Tensile stress | Yield | ISO527-2/50 | 63.0 MPa |
| Tensile modulus | | ISO527-2 | 2450 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179/1eA | 5.5 kJ/m² |
| Charpy Notched Impact Strength | | ISO179/1eA | 6.5 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179/1eU | 230 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179/1eU | 260 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC60093 | 1E+15 ohms |
| Volume resistivity | | IEC60093 | 1E+15 ohms·cm |
| | IEC60250 | 3.80 |
| Dissipation Factor | | IEC60250 | 6E-03 |
| CTI | | IEC60112 | 600 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO11359-2 | 1.1E-04 cm/cm/°C |
| Maximum operating temperature - sortcycle operation | | | 100 °C |
| Heat distortion temperature | | ISO75-2/A | 100 °C |
| melting temperature | | ISO11357-3 | 167 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.