Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.50到1.70 g/cm³ |
| Shrinkage rate | | ISO2577 | 0.50到1.0 % |
| Water absorption rate | | ISO62 | <2.0 % |
| PostShrinkage | | ISO2577 | 1.0到1.5 % |
| Apparent density | | ISO60 | 0.55到0.75 g/cm³ |
| Shrinkage rate | | ISO2577 | 0.80到1.3 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | V-0 |
| Burning wire flammability index | | IEC60695-2-12 | 960 °C |
| Hot filament ignition temperature | | IEC60695-2-13 | 900 °C |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| CompressionMoldingPressure | | | >20.0 MPa |
| CompressionMoldingTemperature | | | 160到180 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | Compression Molded | ISO527-2 | 5000到8000 MPa |
| Tensile modulus | Injection | ISO527-2 | 5000到8000 MPa |
| Tensile stress | | ISO527-2 | 40.0到65.0 MPa |
| Tensile stress | Injection | ISO527-2 | 50.0到90.0 MPa |
| Flexural modulus | Compression Molded | ISO178 | 8000到9000 MPa |
| Flexural modulus | Injection | ISO178 | 8000到9000 MPa |
| Bending stress | Compression Molded | ISO178 | 90.0到120 MPa |
| Bending stress | Injection | ISO178 | 100到130 MPa |
| compression stress | | ISO604 | 200到250 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | Compression Molded | ISO179/1eA | 1.4到2.0 kJ/m² |
| Charpy Notched Impact Strength | Injection | ISO179/1eA | 1.5到2.0 kJ/m² |
| Impact strength of simply supported beam without notch | Compression Molded | ISO179/1eU | 6.0到9.0 kJ/m² |
| Impact strength of simply supported beam without notch | Injection | ISO179/1eU | 8.0到14 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Dissipation Factor | | IEC60250 | 0.30到0.50 |
| Dissipation Factor | | IEC60250 | 0.030到0.050 |
| arc resistance | | ASTMD495 | PLC 5 |
| CTI | | IEC60112 | 600 V |
| | IEC60250 | 11.016.0 |
| | IEC60250 | 7.009.00 |
| Surface Resistivity | | IEC60093 | 1.0E+10到1.0E+11 ohms |
| Volume resistivity | | IEC60093 | 1.0E+11到1.0E+12 ohms·cm |
| dielectric strength | | IEC60243-1 | 15到20 kV/mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/A | 155到180 °C |
| | ISO75-2/C | 110到130 °C |
| | ISO11359-2 | 1.5E-5到3.5E-5 cm/cm/°C |
| thermal conductivity | | ASTME1461 | 0.40到0.50 W/m/K |
| maximum service temperature | | IEC60216 | 160 °C |
| maximum service temperature | | IEC60216 | 135 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.