PC/PBT 5220U-1001 SABIC INNOVATIVE SHANGHAI

Form：Granules | Grade：Injection grade

Properties:

Impact modificationLow temperature impact reChemical resistance

Typical Applications:

chipIndustrial applicationsLawn equipmentGarden equipmentHousehold goodsOutdoor applicationsElectrical fieldElectronic fieldArchitectural application fieldsporting goodsElectrical applianceslensMedical suppliesNursing suppliesPlastic bagAutomotive sectorLighting applicationsNon specific foodAutomotive External Parts

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	chip \| Industrial applications \| Lawn equipment \| Garden equipment \| Household goods \| Outdoor applications \| Electrical field \| Electronic field \| Architectural application field \| sporting goods \| Electrical appliances \| lens \| Medical supplies \| Nursing supplies \| Plastic bag \| Automotive sector \| Lighting applications \| Non specific food \| Automotive External Parts
Properties:	Impact modification \| Low temperature impact re \| Chemical resistance

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Dart impact	23°C, Total Energy	ASTM D3763	60.0	J
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.5 mm	UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength	Yield, 50.0 mm Span6	ASTM D790	84.0	Mpa
bending strength	bending strength	--7,8	ISO 178	80.0	Mpa
Bending modulus	--7	ISO 178	2000	Mpa
Bending modulus	Bending modulus	50.0 mm Span6	ASTM D790	2030	Mpa
elongation	Break	ISO 527-2/50	120	%
	elongation	Break5	ASTM D638	120	%
		elongation	Yield	ISO 527-2/50	4.0	%
		elongation	elongation	Yield5	ASTM D638	4.0	%
tensile strength	Break	ISO 527-2/50	50.0	Mpa
	tensile strength	Break5	ASTM D638	51.0	Mpa
		tensile strength	Yield	ISO 527-2/50	50.0	Mpa
		tensile strength	tensile strength	Yield5	ASTM D638	53.0	Mpa
Tensile modulus	--	ISO 527-2/1	2050	Mpa
	Tensile modulus	--4	ASTM D638	2250	Mpa
	Tensile modulus	Tensile modulus	--3	ASTM D638	2250	Mpa
injection	Test Condition	Test Method	Test Result	Test Unit
Spray nozzle temperature			255 to 270	°C
Processing (melt) temperature			260 to 275	°C
drying temperature			110	°C
drying time			4.0 to 6.0	hr
Suggested maximum moisture content			0.020	%
Suggested injection volume			50 to 80	%
Temperature at the rear of the barrel			245 to 265	°C
Temperature in the middle of the barrel			250 to 270	°C
Temperature at the front of the material cylinder			255 to 275	°C
Mold temperature			65 to 90	°C
Back pressure			0.300 to 0.700	Mpa
Screw speed			50 to 80	rpm
Exhaust hole depth			0.013 to 0.020	mm
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45 MPa, Unannealed, 6.40 mm	ASTM D648	107	°C
Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	84.0	°C
Linear coefficient of thermal expansion	Flow : -40 to 40°C	ASTM E831	9.5E-5	cm/cm/°C
Vicat softening temperature	--	ASTM D152511	122	°C
Linear coefficient of thermal expansion	Across Flow : -40 to 40°C	ASTM E831	9.0E-5	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : -40°C	ISO 11359-2	9.0E-5	cm/cm/°C
RTI Elec		UL 746	75.0	°C
Vicat softening temperature	--	ISO 306/B50	120	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	125	°C
RTI Imp		UL 746	75.0	°C
RTI		UL 746	75.0	°C
Hot deformation temperature	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	99.0	°C
Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span10	ISO 75-2/Af	75.0	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Outdoor applicability		UL 746C	f2
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.15	%
Water absorption rate	Water absorption rate	Saturation, 23°C	ISO 62	0.50	%
Shrinkage rate	Across FlowFlow 2	Internal Method	0.80 - 1.0	%
Shrinkage rate	Shrinkage rate	Flow : 3.20 mm	Internal Method	0.80 - 1.0	%
Melt Volume Flow Rate (MVR)	250°C/5.0 kg	ISO 1133	15.0	cm3/10min
melt mass-flow rate	250°C/5.0 kg	ISO 1133	16	g/10 min
Specific volume		ASTM D792	0.830	cm³/g
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Arc resistance		ASTM D495	PLC 5
Compared to the anti leakage trace index		UL 746	PLC 1
High arc combustion index		UL 746	PLC 0
High voltage arc tracing rate		UL 746	PLC 0
Hot wire ignition		UL 746	PLC 3

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.