Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.36 g/cm³ |
| Water absorption rate | | ISO 62 | 6.00 % |
| Water absorption rate | | ISO 62 | 2.10 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| ball-indentation hardness | | ISO 2039-1 | 181 Mpa |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ISO 180/1A | 10 kJ/m² |
| Impact strength of cantilever beam gap | | ISO 180/1A | 8.4 kJ/m² |
| tensile strength | | ISO 527-2 | 180 Mpa |
| elongation at break | | ISO 527-2 | 3.0 % |
| Tensile modulus | | ISO 527-2 | 9500 Mpa |
| Flexural modulus | | ISO 178 | 8600 Mpa |
| Charpy Notched Impact Strength | | ISO 179/1eA | 10 kJ/m² |
| Flame retardant performance | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL -94 | HB 1.50mm |
| UL flame retardant rating | | UL -94 | HB 2.00mm |
| UL flame retardant rating | | UL -94 | HB 3.00mm |
| GWIT | | IEC 60695-2-12 | 750 °C |
| GWIT | | IEC 60695-2-12 | 800 °C |
| GWIT | | IEC 60695-2-12 | 750 °C |
| Relative temperature of heating wire | | IEC 60695-2-13 | 725 °C |
| Relative temperature of heating wire | | IEC 60695-2-13 | 775 °C |
| Relative temperature of heating wire | | IEC 60695-2-13 | 725 °C |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | IEC 60093 | 1E+13 Ω.cm |
| dielectric constant | | IEC 60250 | 3.80 1MHz |
| Dissipation Factor | | IEC 60250 | 0.025 100HZ |
| Dissipation Factor | | IEC 60250 | 0.025 1MHz |
| Dissipation Factor | | IEC 60112 | 550 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/Bf | 220 °C |
| Heat distortion temperature | | ISO 75-2/Af | 210 °C |
| vicat | | ISO 11357-3 | 220 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.