Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.20 g/cm³ |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| refractive index | | 内部方法 | 1.5850 |
| transmissivity | | DIN 5036 | 86.0 % |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| DegradationTemperature | | | >280 °C |
| SheetTemperature-Forming | | | 180to210 °C |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO 179 | 无断裂 |
| Charpy Notched Impact Strength | | ISO 179 | 10 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2 | 2200 MPa |
| tensile strength | | ISO 527-2 | 60.0 MPa |
| Tensile strain | Break | ISO 527-2 | 80 % |
| bending strength | | ISO 178 | >95.0 MPa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | DIN 53482 | >1.0E+15 ohms |
| Volume resistivity | | DIN 53482 | 1E+15 ohms·cm |
| dielectric strength | | DIN 53481 | >30 kV/mm |
| dielectric constant | | DIN 53483 | 3.00 |
| Dissipation Factor | | DIN 53483 | 8E-04 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| vicat | | ISO 306/A50 | 145 °C |
| Linear coefficient of thermal expansion | | DIN 53328 | 6.5E-05 cm/cm/°C |
| specific heat | | | 1170 J/kg/°C |
| thermal conductivity | | DIN 52612 | 0.20 W/m/K |
| Heat distortion temperature | | ISO 75-2 | 135 °C |
| maximum service temperature | | | 115 °C |
| maximum service temperature | | | 130 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.