Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D1505 | 0.956 g/cm³ |
| melt mass-flow rate | | ASTM D1238 | 0.044 g/10min |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTM D785 | 55 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 290 J/m |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTM D638 | 22.6 Mpa |
| tensile strength | | ASTM D638 | 29.4 Mpa |
| Flexural modulus | | ASTM D747 | 981 Mpa |
| film | Test Condition | Test Method | Test Result |
|---|
| Dart impact | | ASTM D1709 | 200 g |
| film thickness | | | 20 µm |
| tensile strength | | ASTM D882 | 53.9 Mpa |
| tensile strength | | ASTM D882 | 49.0 Mpa |
| elongation | | ASTM D882 | 380 % |
| elongation | | ASTM D882 | 450 % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| brittle temperature | | ASTM D746 | -80.0 °C |
| vicat | | ASTM D15251 | 124 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.