Technical Data Sheet
| Cured Properties | Test Condition | Test Method | Test Result |
|---|
| LapShearStrength | | | 8.14 MPa |
| relative permittivity | | | 4.21 |
| Volume resistivity | | | >5.0E+13 ohms·cm |
| Dissipation Factor | | | 0.016 |
| Shore hardness | | | 77 |
| Uncured Properties | Test Condition | Test Method | Test Result |
|---|
| Color | | | Yellow |
| density | | | 1.32 g/cm³ |
| Viscosity | | | 25to35 Pa·s |
| Curing Time | | | 1.0 hr |
| STORAGE STABILITY | | | 4300 min |
| physical property | Test Condition | Test Method | Test Result |
|---|
| Particle size | | | <20.0 µm |
| thermosetting | Test Condition | Test Method | Test Result |
|---|
| shelf-life | | | 26 wk |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| operate temperature | | | -55-300 °C |
| operate temperature | | | 2.85 GPa |
| operate temperature | | | 2.80 |
| weight loss on heating | | | 0.31 % |
| weight loss on heating | | | 0.78 % |
| weight loss on heating | | | 1.9 % |
| DegradationTemperature | | | 381 °C |
| Shear Strength | | | 23.4 MPa |
| operate temperature | | | -55-200 °C |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Glass Transition Temperature | | | >55.0 °C |
| Linear coefficient of thermal expansion | | | 6.3E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | | | 2E-04 cm/cm/°C |
| Linear coefficient of thermal expansion | | | 0.55 W/m/K |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.