PP Alloy Propafilm™ RGP80 Innovia Films Ltd.
0
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | 内部方法 | 6.0 % | |
| 内部方法 | -1.0 % |
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| gloss | ASTM D2457 | 100 | |
| Haze ratio | ASTM D1003 | 2.0 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| coefficient of friction | ASTM D1894 | 0.30 | |
| ASTM D1894 | 0.30 |
| film | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Water Vapor Transmission Rate | ASTMF1770 | 7.4 g/m²/24hr | |
| CoronaTreatment | 内部方法 | 38 dyne/cm | |
| usage | 内部方法 | 55.0 m²/kg | |
| elongation | ASTM D882 | 130 % | |
| Sealing emphasis | 内部方法 | 0.14 N/mm | |
| Initial sealing temperature | 内部方法 | 116to146 °C | |
| OTr | ASTMF1927 | 58 cm³·mm/m²/atm/24hr | |
| film thickness | 2000 µm | ||
| Secant modulus | ASTM D882 | 2490 MPa | |
| ASTM D882 | 2090 MPa | ||
| tensile strength | ASTM D882 | 230 MPa | |
| ASTM D882 | 190 MPa | ||
| elongation | ASTM D882 | 90 % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.