Technical Data Sheet
physical property | Test Condition | Test Method | Test Result |
---|
Water absorption rate | | | 0.30 % |
Uncured Properties | Test Condition | Test Method | Test Result |
---|
density | | | 1.20to1.24 g/cm³ |
density | | | 1.55to1.58 g/cm³ |
Cured Properties | Test Condition | Test Method | Test Result |
---|
Shore hardness | | ISO 868 | 30to40 |
tensile strength | | ISO 527 | 7.00 MPa |
elongation | Break | ISO 527 | 20 % |
dielectric strength | | IEC 60243 | 38 kV/mm |
relative permittivity | | IEC 60250 | 6.10 |
Volume resistivity | | IEC 60093 | 1E+13 ohms·cm |
thermosetting | Test Condition | Test Method | Test Result |
---|
Thermosetting components | Resin | | 100 |
Thermosetting components | Hardener | | 按重量计算的混合比:16 |
Thermosetting components | | | 5.0to50 min |
Thermosetting components | | | 600to900 cP |
flammability | Test Condition | Test Method | Test Result |
---|
UL flame retardant rating | | UL 94 | V-0 |
Supplementary Information | Test Condition | Test Method | Test Result |
---|
operate temperature | | | -40-130 °C |
Thermal performance | Test Condition | Test Method | Test Result |
---|
thermal conductivity | | ISO 22007-2 | 0.80 W/m/K |
Glass Transition Temperature | | TMA | -4.00 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.