| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ISO 294-4 | 1.1 % |
| Shrinkage rate | | ISO 294-4 | 1.1 % |
| Water absorption rate | | ISO 62 | 0.75 % |
| Water absorption rate | | ISO 62 | 1.6 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Limiting Oxygen Index | | ISO 4589-2 | 25 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2/1A | 4500 Mpa |
| Tensile stress | | ISO 527-2/1A | 80.0 Mpa |
| Tensile strain | | ISO 527-2 | 7.0 % |
| Flexural modulus | | ISO 178 | 3850 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 25 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC 60093 | 5.0E+14 ohms |
| Volume resistivity | | IEC 60093 | 5.0E+14 ohms·cm |
| dielectric strength | | IEC 60243-1 | 30 KV/mm |
| Dissipation Factor | | IEC 60250 | 0.020 |
| CTI | | IEC 60112 | 400 V |
| injection | Test Condition | Test Method | Test Result |
|---|
| drying temperature | | | 80 °C |
| Suggested maximum moisture content | | | 0.20 % |
| Temperature at the rear of the barrel | | | 270 到 280 °C |
| Temperature in the middle of the barrel | | | 275 到 285 °C |
| Temperature at the front of the material cylinder | | | 280 到 290 °C |
| Temperature | | | 70 到 100 °C |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| melting temperature | | ISO 11357-3 | 263 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.