Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.30 g/cm³ |
| Melt volume flow rate | | ISO1133 | 100 cm³/10min |
| Shrinkage rate | | ISO294-4 | 0.80 % |
| Shrinkage rate | | ISO294-4 | 0.60 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | V-2 |
| Burning wire flammability index | | IEC60695-2-12 | 960 °C |
| burning rate | | FMVSS302 | <100 mm/min |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| ReinforcementContent | | ISO1172 | 20 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO527-2/1 | 6000 MPa |
| Tensile stress | Break | ISO527-2/5 | 95.0 MPa |
| Tensile strain | Break | ISO527-2/5 | 4.0 % |
| Flexural modulus | | ISO178 | 5800 MPa |
| Bending stress | | ISO178 | 160 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179/1eA | 3.0 kJ/m² |
| Charpy Notched Impact Strength | | ISO179/1eA | 4.0 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179/1eU | 55 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179/1eU | 40 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/B | 220 °C |
| | ISO75-2/A | 210 °C |
| melting temperature | | DINEN11357-1 | 222 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.