PEI ProPolymers PEI 1110-WHT
0
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTMD792 | 1.35 g/cm³ | |
| melt mass-flow rate | ASTMD1238 | 15 g/10min | |
| Shrinkage rate | ASTMD955 | 0.50到0.80 % | |
| ASTMD955 | 0.60到0.90 % | ||
| Water absorption rate | ASTMD570 | 0.25 % |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | M-Scale | 109 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | Yield | ASTMD638 | 110 MPa |
| elongation | Yield | ASTMD638 | 10 % |
| Break | ASTMD638 | 60 % | |
| Flexural modulus | ASTMD790 | 3720 MPa | |
| bending strength | ASTMD790 | 165 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTMD256 | 53 J/m | |
| ASTMD256 | 6.00 kJ/m² | ||
| Suspended wall beam without notch impact strength | ASTMD256 | 1300 J/m | |
| ASTMD256 | 140 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ASTMD648 | 210 °C | ||
| ASTMD648 | 199 °C | ||
| vicat | ASTMD1525 | 219 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.