PPO EXNL1117BK SABIC INNOVATIVE US

Form：Granules | Grade：Injection grade

Properties:

High temperature resistanHydrolysis resistancewear resistant

Typical Applications:

Instrument panel componentsMechanical Engineeringvalve

Supplier(2)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Instrument panel components \| Mechanical Engineering \| valve
Properties:	High temperature resistan \| Hydrolysis resistance \| wear resistant

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	23°C	ISO 179/1eA	10	kJ/m²
Impact strength of cantilever beam gap	-30°C	ISO 180/1A	4.6	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	9.3	kJ/m²
Dart impact	23°C,TotalEnergy	ASTM D3763	30.0	J
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.5mm	UL 94	V-1
UL flame retardant rating	UL flame retardant rating	2.5mm	UL 94	V-0
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus		ASTM D638	2560	Mpa
Tensile modulus	Tensile modulus		ISO 527-2/1	2810	Mpa
tensile strength	Yield	ASTM D638	67.0	Mpa
	tensile strength	Yield	ISO 527-2/50	65.0	Mpa
		tensile strength	Break	ASTM D638	55.0	Mpa
		tensile strength	tensile strength	Break	ISO 527-2/50	60.0	Mpa
elongation	Yield	ASTM D638	3.6	%
Tensile strain	Yield	ISO 527-2/50	3.3	%
elongation	Break	ASTM D638	5.2	%
Tensile strain	Break	ISO 527-2/50	4.4	%
Bending modulus	50.0mmSpan	ASTM D790	2730	Mpa
Bending modulus	Bending modulus		ISO 178	2650	Mpa
bending strength		ISO 178	100	Mpa
bending strength	bending strength	Yield,50.0mmSpan	ASTM D790	100	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	75.0	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	75.0	°C
Vicat softening temperature		ASTM D152510	96.0	°C
	Vicat softening temperature	--	ISO 306/B50	96.0	°C
	Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	98.0	°C
Linear coefficient of thermal expansion	MD：-40to40°C	ASTME831	7.7E-05	cm/cm/°C
	Linear coefficient of thermal expansion	MD：-40to40°C	ISO 11359-2	7.7E-05	cm/cm/°C
		Linear coefficient of thermal expansion	TD：-40to40°C	ASTME831	7.9E-05	cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：-40to40°C	ISO 11359-2	7.9E-05	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	280°C/2.16kg	ASTM D1238	25	g/10min
Melt Volume Flow Rate (MVR)	280°C/2.16kg	ISO 1133	25.0	cm3/10min
Shrinkage rate	MD：3.20mm	Internal Method	0.50-0.70	%
Water absorption rate	Saturation,23°C	ISO 62	0.060	%
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	9E-03	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top

PPO EXNL1117BK SABIC INNOVATIVE US

Product Description

Certificates

Technical Data Sheet

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index