Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTMD792 | 1.82 g/cm³ |
| Tightening rate | | ASTMD1895 | 2.0 |
| Shrinkage rate | | ASTMD955 | 0.10 % |
| Water absorption rate | | ASTMD570 | 0.080 % |
| thermosetting | Test Condition | Test Method | Test Result |
|---|
| Shelf Life | | | 26 wk |
| stripping time | | | 5.0到10 min |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Compressive Modulus | | ASTMD695 | 13100 MPa |
| compressive strength | | ASTMD695 | 172 MPa |
| tensile strength | | ASTMD638 | 241 MPa |
| Flexural modulus | | ASTMD790 | 17900 MPa |
| bending strength | | ASTMD790 | 455 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTMD256 | 1900 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ASTMD257 | 3E+14 ohms·cm |
| dielectric strength | | ASTMD149 | 16 kV/mm |
| dielectric constant | | ASTMD150 | 4.30 |
| Dissipation Factor | | ASTMD150 | 7E-03 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat Deflection Temperature | | ASTMD648 | 302 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.