Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.18 g/cm³ |
| melt mass-flow rate | | ISO 1133 | 46 g/10min |
| Melt volume flow rate | | ISO 1133 | 45 cm3/10min |
| Shrinkage rate | | ISO 294-4 | 0.75 % |
| Shrinkage rate | | ISO 294-4 | 0.75 % |
| Water absorption rate | | ISO 62 | 0.3 % |
| Water absorption rate | | ISO 62 | 0.12 % |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| refractive index | | ISO 489 | 1.578 |
| transmittance | | ISO 13468-2 | 89 % |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| electrolytic corrosion | | IEC 60426 | A1 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO 179/1eU | No Break |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | No Break |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-1-2 | 2400 Mpa |
| tensile strength | | ISO 527-2/50 | 68 Mpa |
| Tensile strain | | ISO 527-2/50 | 6.2 % |
| Nominal tensile fracture strain | | ISO 527-2/50 | > 50 % |
| Flexural modulus | | ISO 178 | 2400 Mpa |
| bending strength | | ISO 178 | 100 Mpa |
| ball-indentation hardness | | ISO 2039-1 | 120 Mpa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC 60093 | 10000000000000000 ohms |
| Volume resistivity | | IEC 60093 | 100000000000000000 ohms·cm |
| dielectric strength | | IEC 60243-1 | 35 KV/mm |
| relative permittivity | | IEC 60250 | 3 |
| relative permittivity | | IEC 60250 | 2.9 |
| Dissipation Factor | | IEC 60250 | 0.001 |
| Dissipation Factor | | IEC 60250 | 0.009 |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 2 |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 4 |
| UL flame retardant rating | | UL 94 | HB |
| UL flame retardant rating | | UL 94 | HB |
| Glow wire combustion index (GWFI) | | IEC 60695-2-12 | 900 °C |
| Limiting Oxygen Index | | ISO 4589-2 | 26 % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/A | 138 °C |
| vicat | | ISO 306/B120 | 158 °C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 0.000065 1/℃ |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 0.000065 1/℃ |
| Relative Heat Index (RTI) | | UL 746 | 140 °C |
| Relative Heat Index (RTI) | | UL 746 | 140 °C |
| Relative Heat Index (RTI) | | UL 746 | 130 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.