Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Specific volume | | | 0.957 cm³/g |
| Shrinkage rate | | ASTMD2566 | 0.14 % |
| Solid content by volume | | | 100 % |
| thermosetting | Test Condition | Test Method | Test Result |
|---|
| Resin | | 按重量计算的混合比:69 |
| Hardener | | 按重量计算的混合比:31 |
| | | 10 min |
| | | 6000 cP |
| Demold Time | | 300 min |
| Uncured Properties | Test Condition | Test Method | Test Result |
|---|
| Curing Time | | | 16 hr |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore A | ASTMD2240 | 97 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Wear amount | | | 330 mg/1000cycles |
| elastomer | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTMD412 | 19.3 MPa |
| elongation | Break | ASTMD412 | 500 % |
| tear strength | | ASTMD624 | 72.7 kN/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric strength | | ASTMD149 | 14 kV/mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| MaximumOperatingTemperature | | | 82 °C |
| MaximumOperatingTemperature | | | 49 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.