PBT 3300D CELANESE USA

Form：Granules | Grade：Enhanced level

Properties:

Glass fiber reinforcedFiller: Glass fiber reinf30%Filler by weight

Typical Applications:

Automotive sectorcurrency

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Automotive sector \| currency
Properties:	Glass fiber reinforced \| Filler: Glass fiber reinf \| 30% \| Filler by weight

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	23°C	ISO 179/1eA	8.5	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30°C	ISO 179/1eA	8.5	kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	45	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	46	kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180/1A	7.5	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
Extreme Oxygen Index		ISO 4589-2	20	%
UL flame retardant rating	0.710mm	UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
-40°C	-40℃	ASTM D638	11000	Mpa
0°C		ASTM D638	10500	Mpa
bending strength	23°C	ISO 178	210	Mpa
crack		ISO 527-2/1A/5	2.5	%
Bending modulus	23°C	ISO 178	9700	Mpa
Fracture, 121 ° C	Break,121°C	ASTM D638	4.3	%
Fracture, 80 ° C	Break,80°C	ASTM D638	3.9	%
Fracture, 0 ° C	Break,0°C	ASTM D638	1.9	%
Fracture, 23 ° C		ASTM D638	2.0	%
Broken- 40°C		ASTM D638	1.9	%
23°C		ASTM D638	9650	Mpa
80°C	80℃	ASTM D638	4830	Mpa
121°C	121℃	ASTM D638	3760	Mpa
Broken- 40°C		ASTM D638	190	Mpa
Fracture, 0 ° C	Break,0°C	ASTM D638	159	Mpa
Fracture, 23 ° C		ASTM D638	134	Mpa
Fracture, 80 ° C	Break,80°C	ASTM D638	77.2	Mpa
Fracture, 121 ° C	Break,121°C	ASTM D638	61.4	Mpa
crack		ISO 527-2/1A/5	130	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	MD	ISO 11359-2	2.5E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	ISO 11359-2	1E-04	cm/cm/°C
Melting temperature		ISO 11357-3	225	°C
Vicat softening temperature		ISO 306/B50	220	°C
Glass transition temperature		ISO 11357-2	60.0	°C
1.8MPa, unannealed		ASTM D648	206	°C
1.8MPa, unannealed	1.8MPa, unannealed		ISO 75-2/A	205	°C
8.0Mpa, unannealed		ISO 75-2/C	150	°C
0.45MPa, annealed		ASTM D648	228	°C
0.45MPa, unannealed		ISO 75-2/B	225	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
	Flow	ISO 294-4	0.30to0.70	%
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.20	%
Vertical flow direction		ISO 294-4	0.70to1.1	%
flow		ASTM D955	0.30to0.50	%
melt mass-flow rate		ASTM D1238	16	g/10min
density		ASTMD792	1.53	g/cm³
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
1MHz	1MHz	ASTMD150	0.016
100Hz	100Hz	IEC 60250	2.2E-03
1MHz	1MHz	IEC 60250	4.10
1MHz	1MHz	1MHz	ASTM D150	3.70
100Hz	100Hz	IEC 60250	4.50
--3		ASTM D149	22	KV/mm
Surface resistivity		IEC 60093	>1.0E+15	ohms
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	M-Sale	ISO 2039-2	90

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.