PC/ABS 63000CTC SABIC INNOVATIVE US

Form：Granules

Properties:

High mobilityHigh impact resistance

Typical Applications:

Automotive interior partsElectrical applicationschip

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Automotive interior parts \| Electrical applications \| chip
Properties:	High mobility \| High impact resistance

Certificates

No Data...

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result	Test Unit
turbidity	2540μm	ASTM D1003	25	%
transmissivity	2540μm	ASTM D1003	77.0	%
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength	Break,50.0mmSpan	ASTM D790	52.0	Mpa
Bending modulus	--6	ISO 178	1150	Mpa
elongation	Break4	Internal Method	200	%
tensile strength	Yield	ISO 527-2/5	34.0	Mpa
tensile strength	tensile strength	Yield3	ASTM D638	35.0	Mpa
Tensile modulus	--	ISO 527-2/1	1190	Mpa
Tensile modulus	Tensile modulus	--2	ASTM D638	1170	Mpa
Bending modulus	50.0mmSpan5	ASTM D790	1170	Mpa
elongation	Break	ISO 527-2/5	140	%
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	TD:23to60°C	ISO 11359-2	1.4E-04	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD:23to60°C	ISO 11359-2	1.2E-04	cm/cm/°C
Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	75.0	°C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed,6.40mm	ASTM D648	84.0	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.70	%
Shrinkage rate	TD	Internal Method	0.60	%
Shrinkage rate	Shrinkage rate	MD	Internal Method	0.60	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
StaticDecay		FTMS101B	2.0	sec
Volume resistivity		ASTM D257	8.0E+9-3.0E+11	ohms·cm
Surface resistivity		ASTM D257	9.0E+9-4.0E+11	ohms

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.