Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 0.950 g/cm³ |
| density | | ISO 1183 | 0.950 g/cm³ |
| melt mass-flow rate | | ASTM D1238 | 1.1 g/10min |
| melt mass-flow rate | | ISO 1133 | 1.1 g/10min |
| IonType | | | Zinc |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ISO 868 | 60 |
| Shore hardness | | ASTM D2240 | 60 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| Haze ratio | | ASTM D1003 | 26 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Flexural modulus | | ASTM D790 | 260 MPa |
| wear resistance | | ASTM D1630 | 290 |
| Flexural modulus | | ASTM D790 | 655 MPa |
| tensile strength | | ASTM D638 | 25.5 MPa |
| tensile strength | | ISO 527-2 | 25.5 MPa |
| elongation | | ASTM D638 | 410 % |
| Tensile strain | | ISO 527-2 | 410 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D1822 | 1030 kJ/m² |
| Impact strength of cantilever beam gap | | ASTM D1822 | 1190 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| vicat | | ASTM D1525 | 74.0 °C |
| vicat | | ISO 306 | 74.0 °C |
| melting temperature | | ASTM D3418 | 96.0 °C |
| melting temperature | | ISO 3146 | 96.0 °C |
| FreezingPoint | | ASTM D3418 | 76 °C |
| FreezingPoint | | ISO 3146 | 76 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.