Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | g/cm³ | 1.29 -- |
| Water absorption rate | | % | 5.5 -- |
| Water absorption rate | | % | 1.7 -- |
| Water absorption rate | | mg | 30.0 -- |
| Water absorption rate | | mg | 56.0 -- |
| hardness | Test Condition | Test Method | Test Result |
|---|
| ball-indentation hardness | | MPa | 165 -- |
| Rockwell hardness | | | 76 -- |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | | HB -- |
| UL flame retardant rating | | | HB -- |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile creep modulus | | MPa | 26.0 18.0 |
| compression stress | | MPa | 90.0 -- |
| compression stress | | MPa | 55.0 -- |
| compression stress | | MPa | 28.0 -- |
| Tensile modulus | | MPa | 5900 3200 |
| tensile strength | | MPa | 100 75.0 |
| Tensile strain | | % | 5.0 12 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | kJ/m² | 6.0 -- |
| Impact strength of simply supported beam without notch | | kJ/m² | >50 -- |
| Impact strength of cantilever beam gap | | kJ/m² | 6.0 11 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ohms·cm | >1.0E+14 >1.0E+13 |
| dielectric strength | | kV/mm | 30 20 |
| relative permittivity | | | 3.90 6.90 |
| relative permittivity | | | 3.60 3.90 |
| Dissipation Factor | | | 0.012 0.19 |
| Dissipation Factor | | | 0.014 0.040 |
| Surface Resistivity | | ohms | >1.0E+13 >1.0E+12 |
| Compared to the Leakage Tracking Index (CTI) | | V | PLC 1 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | °C | 150 -- |
| melting temperature | | °C | 255 -- |
| Linear coefficient of thermal expansion | | cm/cm/°C | 5E-05 -- |
| Linear coefficient of thermal expansion | | cm/cm/°C | 6E-05 -- |
| thermal conductivity | | W/m/K | 0.30 -- |
| Minimum operating temperature | | °C | -20 -- |
| maximum service temperature | | °C | 120 -- |
| maximum service temperature | | °C | 240 -- |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare