PP TU 76 V Ducor Petrochemicals BV
0
- Usages:Thin walled packaginghousehold goods
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO 1183 | 0.910 g/cm³ | |
| melt mass-flow rate | ISO 1133 | 48 g/10min |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ball-indentation hardness | ISO 2039-1 | 44.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | 4.0 kJ/m² | |
| ISO 179/1eA | 4.5 kJ/m² | ||
| ISO 179/1eA | 9.0 kJ/m² | ||
| ISO 179/1eA | 20 kJ/m² | ||
| Impact strength of simply supported beam without notch | ISO 179/1eU | 130 kJ/m² | |
| ISO 179/1eU | 150 kJ/m² | ||
| ISO 179/1eU | 无断裂 | ||
| ISO 179/1eU | 无断裂 | ||
| Impact strength of cantilever beam gap | ISO 180/1A | 4.5 kJ/m² | |
| ISO 180/1A | 5.5 kJ/m² | ||
| ISO 180/1A | 9.0 kJ/m² | ||
| ISO 180/1A | 18 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 950 MPa | |
| tensile strength | Yield | ISO 527-2/50 | 19.0 MPa |
| Tensile strain | Yield | ISO 527-2/50 | 5.0 % |
| Break | ISO 527-2/50 | >50 % | |
| shear modulus | ISO 6721-2 | 500 MPa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| vicat | ISO 306/A | 142 °C | |
| ISO 306/B | 56.0 °C | ||
| melting temperature | ISO 3146 | 163 °C | |
| Heat distortion temperature | ISO 75-2/B | 78.0 °C | |
| ISO 75-2/A | 48.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.