Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D1505 | 1.42 g/cm³ |
| Shrinkage rate | | ASTM D955 | 4E-03 % |
| Water absorption rate | | ASTM D570 | 2.9 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| Limiting Oxygen Index | | ASTM D2863 | 38 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| coefficient of friction | Itself - Static | ASTM D1894 | 0.50 |
| film | Test Condition | Test Method | Test Result |
|---|
| film thickness | | | 76 µm |
| Secant modulus | | ASTM D882 | 3170 MPa |
| tensile strength | Break | ASTM D882 | 241 MPa |
| elongation | Break | ASTM D882 | 95 % |
| Elmendorf tear strength | | ASTM D1922 | 24 g |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric strength | | ASTM D149 | 180 kV/mm |
| dielectric constant | | ASTM D150 | 3.40 |
| Dissipation Factor | | ASTM D150 | 1.4E-03 |
| Hot wire ignition (HWI) | | UL 746 | PLC 0 sec |
| Volume resistivity | | ASTM D257 | 8E+14 ohms·cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| specific heat | | ASTMC351 | 1100 J/kg/°C |
| RTI Elec | | UL 746 | 240 °C |
| RTI | | UL 746 | 200 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare