EVOH FP201B
0
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| EthyleneContent | 内部方法 | 32.0 mol% | |
| density | ISO1183 | 1.19 g/cm³ | |
| melt mass-flow rate | ISO1133 | 0.90 g/10min |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile strain | ISO527-2 | 43 % | |
| Tensile modulus | ISO527-2 | 2600 MPa | |
| Tensile stress | ISO527-2 | 73.0 MPa | |
| ISO527-2 | 32.0 MPa | ||
| Tensile strain | ISO527-2 | 12 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile impact strength | ASTMD1822 | 110 kJ/m² | |
| ASTMD1822 | 390 kJ/m² |
| film | Test Condition | Test Method | Test Result |
|---|---|---|---|
| oxygen permeability | ISO14663-2 | 0.010 cm³·mm/m²/atm/24hr |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Glass Transition Temperature | ISO11357-2 | 69.0 °C | |
| vicat | ISO306 | 173 °C | |
| melting temperature | ISO11357-3 | 183 °C | |
| Crystallization peak temperature | ISO11357-3 | 161 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.