Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 0.479 g/cm³ |
| Shrinkage rate | | ASTM D955 | 0.30to0.50 % |
| thermosetting | Test Condition | Test Method | Test Result |
|---|
| Thermosetting components | | | 按重量计算的混合比:120 |
| Thermosetting components | | | 100 |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ASTM D2240 | 56 |
| Shore hardness | | ASTM D2240 | 64 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| bending strength | | ASTM D790 | 26.2 MPa |
| compressive strength | | ASTM D695 | 18.6 MPa |
| compressive strength | | ASTM D695 | 14.5 MPa |
| tensile strength | | ASTM D638 | 13.8 MPa |
| tensile strength | | ASTM D638 | 12.4 MPa |
| elongation | | ASTM D638 | 7.0 % |
| elongation | | ASTM D638 | 7.0 % |
| Flexural modulus | | ASTM D790 | 717 MPa |
| Flexural modulus | | ASTM D790 | 689 MPa |
| bending strength | | ASTM D790 | 24.1 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | 内部方法 | 9.5 kJ/m² |
| Impact strength of simply supported beam without notch | | 内部方法 | 8.8 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 80.0 °C |
| Heat distortion temperature | | ASTM D648 | 90.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.