ABS

ABS CEVIAN® T150 DAICEL JAPAN

Properties:
transparent
Usages:
Products used for transparency
Compare

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result
Transmittance rate		ASTM D-1003	88 %

Other performance	Test Condition	Test Method	Test Result
JHOPA			抗PL

Basic Performance	Test Condition	Test Method	Test Result
melt mass-flow rate	220℃,10kg	ISO 1133	29 g/10min
Water absorption rate		ISO 62	0.3 %
density		ISO 1183	1.07

mechanical properties	Test Condition	Test Method	Test Result
tensile strength		ISO 527	45 Mpa
bending strength		ISO 178	65 Mpa
Bending modulus		ISO 178	1900 Mpa
Charpy Notched Impact Strength	23℃	ISO 179/1eA	15 KJ/m
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30℃	ISO 179/1eA	7 KJ/m
Impact strength of cantilever beam gap	23℃,6.4mm	ASTM D-256	150 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	-30℃,6.4mm	ASTM D-256	70 J/m
Rockwell hardness		ISO 2039	R108

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	1.80MPa,12.7mm	ISO 75/A	76 °C
Hot deformation temperature	Hot deformation temperature	1.82MPa,12.7mm	ASTM D-648	86 °C
Ball indentation temperature			90 °C
Combustibility		UL 94	HB

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate		ASTM D-955	0.4-0.6 %

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.