Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ASTMD955 | 0.40to0.60 % |
| Shrinkage rate | | ISO294-4 | 0.60 % |
| Water absorption rate | | ISO62 | 0.10 % |
| Water absorption rate | | ASTMD570 | 0.070 % |
| intrinsic viscosity | | 内部方法 | 0.88 dl/g |
| density | | ASTMD792 | 1.33 g/cm³ |
| density | | ISO1183 | 1.33 g/cm³ |
| melt mass-flow rate | | ASTMD1238 | 8.1 g/10min |
| melt mass-flow rate | | ISO1133 | 15 g/10min |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | ASTMD785 | 88 |
| Rockwell hardness | | ISO2039-2 | 88 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| transmissivity | | ASTMD1003 | 85.0 % |
| Haze ratio | | ASTMD1003 | 1.5 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | V-2 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTMD638 | 60.0 MPa |
| Tensile stress | | ISO527-2 | 60.0 MPa |
| elongation | | ASTMD638 | 460 % |
| Tensile strain | | ISO527-2 | 300 % |
| Flexural modulus | | ASTMD790 | 2850 MPa |
| Flexural modulus | | ISO178 | 2900 MPa |
| bending strength | | ASTMD790 | 92.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179/1eA | 3.5 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/B | 75.0 °C |
| melting temperature | | ISO11357-3 | 230 °C |
| melting temperature | | ASTMD1525 | 234 °C |
| | ASTMD696 | 6E-05 cm/cm/°C |
| | ASTMD648A | 77.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.