HIPS HIPS-622 SECCO SHANGHAI
458
- Properties:heat-resistingHigh impact resistance
- Usages:Food packagingCupsElectrical componentsfurniture
- Certificates:ULSGS
Compare
View PricesTechnical Data Sheet
| other | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 高抗冲性、改进耐热性。食品包装、杯子、电器元件、家具 |
| Basic performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO 1183/1987 | 1030 kg/m3 | |
| melt mass-flow rate | ISO 1133/1997 | 4.8 g/10min |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| elongation | ISO 527-2/1993 | 50 % | |
| tensile yield strength | ISO 527-2/1993 | 25 Mpa | |
| Anti impact strength of cantilever beam | ISO 180/1993 | 1150 J/m | |
| Flexural modulus | ISO 178/1993 | 1700 Mpa | |
| ISO 180/1993 | 125 J/m | ||
| Charpy impact strength | ASTM D256/ISO 179 | 125 kg·cm/cm(J/M)ft·lb/in | |
| ASTM D256/ISO 179 | 1150 kg·cm/cm(J/M)ft·lb/in | ||
| elongation at break | ASTM D638/ISO 527 | 50 % | |
| tensile strength | ASTM D638/ISO 527 | 25 kg/cm²(MPa)[Lb/in²] |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.03 | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 4.8 g/10min |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| vicat | ISO 306/1994 | 90 °C | |
| ISO 306/1994 | 1030 °C | ||
| ISO 75-2/1993 | 80 °C | ||
| ASTM D648/ISO 75 | 80 ℃（℉） | ||
| vicat | ASTM D1525/ISO R306 | 90 ℃（℉） |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.