Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.25 g/cm³ |
| melt mass-flow rate | | ASTM D1238 | 18 g/10 min |
| Shrinkage rate | | ASTM D955 | 0.20 - 0.40 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTM D785 | 124 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| UL flame retardant rating | | UL 94 | V-0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTM D638 | 83.4 Mpa |
| Flexural modulus | | ASTM D790 | 3920 Mpa |
| bending strength | | ASTM D790 | 137 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 78 J/m |
| injection | Test Condition | Test Method | Test Result |
|---|
| drying temperature | | | 100 to 200 °C |
| drying time | | | 3.0 to 5.0 hr |
| Suggested maximum moisture content | | | 0.020 % |
| Temperature at the rear of the barrel | | | 270 to 300 °C |
| Temperature in the middle of the barrel | | | 280 to 310 °C |
| Temperature at the front of the material cylinder | | | 290 to 330 °C |
| Spray nozzle temperature | | | 290 to 330 °C |
| Processing (melt) temperature | | | 300 to 340 °C |
| Temperature | | | 90 to 120 °C |
| Back pressure | | | 0.981 to 3.92 Mpa |
| screw speed | | | 40 to 70 rpm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 138 °C |
| RTI Elec | | UL 746 | 120 °C |
| RTI Imp | | UL 746 | 90.0 °C |
| RTI | | UL 746 | 105 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.