Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Specific volume | | ASTMD792 | 0.750 cm³/g |
| Melt volume flow rate | | ISO1133 | 8.00 cm3/10min |
| Shrinkage rate | | 内部方法 | 1.0到1.4 % |
| Shrinkage rate | | 内部方法 | 0.80到1.1 % |
| Shrinkage rate | | 内部方法 | 1.2到1.6 % |
| Shrinkage rate | | 内部方法 | 0.90到1.3 % |
| Water absorption rate | | ASTMD570 | 0.080 % |
| Outdoor applicability | | UL746C | f2 |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTMD785 | 117 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| UL flame retardant rating | | UL94 | V-0 |
| UL flame retardant rating | | UL94 | 5VA |
| Limiting Oxygen Index | | ASTMD2863 | 30 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile strength 5 | | ASTMD638 | 48.3 Mpa |
| Tensile strength 5 | | ASTMD638 | 48.3 Mpa |
| | ASTMD638 | 110 % |
| Bending modulus 6 | | ASTMD790 | 2070 Mpa |
| Bending strength 6 | | ASTMD790 | 82.7 Mpa |
| Bending strength 6 | | ASTMD790 | 82.7 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Suspended wall beam without notch impact strength | | ASTMD4812 | 3200 J/m |
| Falling hammer impact | | ASTMD3029 | 43.4 J |
| Falling hammer impact | | ASTMD3029 | 43.4 J |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ASTMD257 | >1.2E+16 ohms·cm |
| dielectric strength | | ASTMD149 | 25 KV/mm |
| dielectric strength | | ASTMD149 | 19 KV/mm |
| dielectric strength | | ASTMD149 | 19 KV/mm |
| dielectric constant | | ASTMD150 | 3.20 |
| dielectric constant | | ASTMD150 | 3.20 |
| Dissipation Factor | | ASTMD150 | 3E-03 |
| Dissipation Factor | | ASTMD150 | 0.030 |
| Arc resistance 8 | | ASTMD495 | PLC6 |
| Compared to the Leakage Tracking Index (CTI) | | UL746 | PLC 2 |
| High arc combustion index (HAI) | | UL746 | PLC 3 |
| High Voltage Arc Traceability Rate (HVTR) | | UL746 | PLC 3 |
| Hot wire ignition (HWI) | | UL746 | PLC 2 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTMD648 | 138 °C |
| Heat distortion temperature | | ASTMD648 | 98.9 °C |
| | ASTME831 | 9.2E-05 cm/cm/°C |
| | ASTME831 | 1.2E-04 cm/cm/°C |
| RTI Elec | | UL746 | 120 °C |
| RTI Imp | | UL746 | 120 °C |
| RTI | | UL746 | 140 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare
View Prices