COC

COC ZEONEX® F52R ZEON JAPAN

Properties:
Ozone resistantLow tenderness
Usages:
Automotive Applicationspipeline
Certificates:
UL
Compare View Prices

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result
Refractive index		ASTM D542	1.535
transmissivity	3000μm	ASTM D1003	92.0 %
Transmittance rate		ASTM D1003/ISO 13468	92% %
Refractive index		ASTM D542/ISO 489	1.535

other	Test Condition	Test Method	Test Result
remarks			光学镜片
characteristic			高折射率耐环境性能
Color			透明
purpose			光学镜头光学镜片

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO 527-2	2500 Mpa
tensile strength		ISO 527-2	45.0 Mpa
Tensile strain	Break	ISO 527-2	2.0 %
Bending modulus		ISO 178	2500 Mpa
Impact strength of cantilever beam gap		ASTM D256/ISO 179	19 kg·cm/cm(J/M)ft·lb/in
elongation		ASTM D638/ISO 527	2 %
Bending modulus		ASTM D790/ISO 178	2400 kg/cm²(MPa)[Lb/in²]
bending strength		ASTM D790/ISO 178	109 kg/cm²(MPa)[Lb/in²]
tensile strength		ASTM D638/ISO 527	45 kg/cm²(MPa)[Lb/in²]
Tensile modulus		ASTM D638/ISO 527	3000 kg/cm²(MPa)[Lb/in²]

thermal performance	Test Condition	Test Method	Test Result
Glass transition temperature		JISK7121	156 °C
Linear coefficient of thermal expansion	MD	ASTME831	6E-05 cm/cm/°C
Hot deformation temperature	HDT	ASTM D648/ISO 75	156 ℃（℉）
Hot deformation temperature	Hot deformation temperature	HDT	ASTM D648/ISO 75	144 ℃（℉）
Combustibility (rate)		UL 94	HB

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	280°C/2.16kg	JISK6719	22 g/10min
Water absorption rate	Equilibrium	ASTM D570	<0.010 %
density		ASTM D792/ISO 1183	1.02
Water absorption rate		ASTM D570/ISO 62	<0.01 %

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

COC ZEONEX® F52R ZEON JAPAN

Technical Data Sheet