PP Homopolymer SAXALEN™ PPH319FX21
0
- Usages:Thin walled components
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO1183 | 0.910 g/cm³ | |
| Melt volume flow rate | ISO1133 | 28.0 cm³/10min |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL94 | V-2 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of cantilever beam gap | ISO180/1A | 4.0 kJ/m² | |
| Notched Izod impact strength | ISO180/1U | 13 kJ/m² | |
| ISO180/1U | 55 kJ/m² | ||
| Impact strength of cantilever beam gap | ISO180/1A | 2.0 kJ/m² | |
| Charpy Notched Impact Strength | ISO179/1eA | 2.0 kJ/m² | |
| ISO179/1eA | 4.0 kJ/m² | ||
| Impact strength of simply supported beam without notch | ISO179/1eU | 15 kJ/m² | |
| ISO179/1eU | 85 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO527-2/1 | 2100 MPa | |
| Tensile stress | Break | ISO527-2/50 | 36.0 MPa |
| Tensile strain | Break | ISO527-2/50 | 6.0 % |
| Flexural modulus | ISO178 | 1200 MPa | |
| Bending stress | ISO178 | 35.0 MPa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | ISO75-2/A | 120 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.