Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTMD792 | 1.05 g/cm³ |
| melt mass-flow rate | | ASTM D1238 | 6.0 g/10min |
| Melt volume flow rate | | ISO 1133 | 6.00 cm³/10min |
| flow | | ASTM D955 | 0.20to0.60 % |
| Water absorption rate | | ASTMD570 | 0.10 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Hardness (Rockwell M) | | ASTM D785 | 70 |
| Hardness (Rockwell M) | | ASTM D785 | 70 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| refractive index | | ASTMD542 | 1.560 |
| transmissivity | | ASTM D1003 | 91.0 % |
| Haze ratio | | ASTM D1003 | 2.5 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 110 J/m |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| yield | | ASTM D638 | 27.6 MPa |
| yield | | ISO 527-2 | 28.0 MPa |
| elongation | Break | ASTM D638 | 40 % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| vicat | | ASTM D15251 | 97.8 °C |
| maximum service temperature | | | 250 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.