Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Apparent density | | ISO60 | 0.38 | g/cm³ |
| Shrinkage rate | | 内部方法 | 4.3 | % |
| Average particle size | | ISO13320 | 25 | µm |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Shore hardness | 邵氏D | ISO868 | 56 | |
| Tensile modulus | | ISO527-2 | 600 | Mpa |
| Load deformation | 15MPa2 | ASTMD621 | 16.0 | % |
| Load deformation | 15MPa3 | ASTMD621 | 17.0 | % |
| Load deformation | 15MPa4 | ASTMD621 | 10.0 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Linear coefficient of thermal expansion | MD：30到100°C | DIN53752 | 1.2E-04 | cm/cm/°C |
| Linear coefficient of thermal expansion | MD：30到200°C | DIN53752 | 1.4E-04 | cm/cm/°C |
| Linear coefficient of thermal expansion | MD：30到260°C | DIN53752 | 1.7E-04 | cm/cm/°C |
| thermal conductivity | | DIN52612 | 0.22 | W/m/K |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Surface resistivity | | IEC60093 | 1E+17 | ohms |
| Volume resistivity | | IEC60093 | 1E+18 | ohms·cm |
| Dielectric strength | 0.100mm | ISO12086 | 88 | KV/mm |
| film | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile strength | 100µm | ISO527-3 | 42.0 | Mpa |
| elongation | 断裂,100µm | ISO527-3 | 430 | % |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | | UL94 | V-0 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.