Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ISO 294-4 | 0.55 % |
| Water absorption rate | | ISO 62 | 0.95 % |
| Water absorption rate | | ISO 62 | 0.24 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| ball-indentation hardness | | ISO 2039-1 | 99 Mpa |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| Yellowness Index | | DIN 6167 | 15 YI |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 90 kJ/m² |
| Impact strength of cantilever beam gap | | ISO 180/1A | 22 kJ/m² |
| Impact strength of cantilever beam gap | | ISO 180/1A | 7 kJ/m² |
| elongation at break | | ISO 527-2 | 2.4 % |
| Tensile modulus | | ISO 527-2 | 2300 Mpa |
| bending strength | | ISO 178 | 65 Mpa |
| Charpy Notched Impact Strength | | ISO 179/1eA | 19 kJ/m² |
| Charpy Notched Impact Strength | | ISO 179/1eA | 7 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 130 kJ/m² |
| Flame retardant performance | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL -94 | HB 0.80mm |
| UL flame retardant rating | | UL -94 | HB 1.50mm |
| UL flame retardant rating | | UL -94 | HB 3.00mm |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | IEC 60093 | 1E+15 Ω.cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/B | 95 °C |
| Heat distortion temperature | | ISO 75-2/A | 92 °C |
| vicat | | ISO 306/A50 | 102 °C |
| vicat | | ISO 306/B50 | 95 °C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 8E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 1.1E-04 cm/cm/°C |
| Linear coefficient of thermal expansion | | DIN 52612 | 0.17 W/m/K |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.