PP Copolymer CC6057

Compare

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result
melt mass-flow rate		ISO 1133	1.0 g/10min
density		内部方法	1.13 g/cm³
melt mass-flow rate		ISO 1133	15 g/10min
melt mass-flow rate	melt mass-flow rate		ISO 1133	74 g/10min

Mechanical properties	Test Condition	Test Method	Test Result
tensile strength		ISO 527-2	26.0 MPa
	tensile strength		ISO 527-2	27.0 MPa
	tensile strength	tensile strength		ISO 527-2	28.0 MPa
Tensile strain		ISO 527-2	120 %
	Tensile strain		ISO 527-2	76 %
	Tensile strain	Tensile strain		ISO 527-2	44 %
Flexural modulus		ISO 178	1320 MPa
	Flexural modulus		ISO 178	1380 MPa
	Flexural modulus	Flexural modulus		ISO 178	1460 MPa

Impact resistance	Test Condition	Test Method	Test Result
Suspended wall beam without notch impact strength		ISO 180	71 kJ/m²
	Suspended wall beam without notch impact strength		ISO 180	67 kJ/m²
	Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength		ISO 180	73 kJ/m²

Electrical performance	Test Condition	Test Method	Test Result
Surface Resistivity		内部方法	20 ohms
	Surface Resistivity		内部方法	3E+05 ohms
		Surface Resistivity		内部方法	2E+03 ohms
		Surface Resistivity	Surface Resistivity		内部方法	3E+02 ohms
Volume resistivity		内部方法	1.0 ohms·cm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.