PA66 R530 ASCEND USA

Form：Granules | Grade：Extrusion grade

Properties:

Filler: Glass fiber reinf30%Filler by weight

Typical Applications:

Parts under the hood of a car

Supplier(1)

Product Description

Certificates(2)

Datasheet

Product Description

Typical Applications:	Parts under the hood of a car
Properties:	Filler: Glass fiber reinf \| 30% \| Filler by weight

Certificates

RoHS

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	23°C	ISO 179	75	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179	65	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.75mm	UL 94	HB
	UL flame retardant rating	1.5mm	UL 94	HB
	UL flame retardant rating	UL flame retardant rating	3.0mm	UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Poisson's Ratio	23°C	ISO 527	0.40
bending strength	23°C	ISO 178	270	Mpa
Bending modulus	23°C	ISO 178	9600	Mpa
Tensile strain	Break,23°C	ISO 527-2	3.0	%
tensile strength	Break,23°C	ISO 527-2	195	Mpa
Tensile modulus	23°C	ISO 527-2	10000	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
RTI Imp	3.0mm	UL 746	105	°C
	RTI Imp	1.5mm	UL 746	85.0	°C
	RTI Imp	RTI Imp	0.75mm	UL 746	85.0	°C
RTI Elec	3.0mm	UL 746	120	°C
	RTI Elec	1.5mm	UL 746	120	°C
	RTI Elec	RTI Elec	0.75mm	UL 746	120	°C
Linear coefficient of thermal expansion	TD：23to55°C,2.00mm	ISO 11359-2	1.1E-04	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：23to55°C,2.00mm	ISO 11359-2	2.2E-05	cm/cm/°C
Melting temperature		ISO 11357-3	260	°C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	250	°C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	260	°C
RTI Str	0.75mm	UL 746	115	°C
	RTI Str	1.5mm	UL 746	120	°C
	RTI Str	RTI Str	3.0mm	UL 746	120	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	1.9	%
Water absorption rate	Water absorption rate	23°C,24hr	ISO 62	0.90	%
Shrinkage rate	MD:23°C,2.00mm	ISO 294-4	0.40	%
Shrinkage rate	Shrinkage rate	TD:23°C,2.00mm	ISO 294-4	0.90	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Hot wire ignition	0.75mm	UL 746	PLC 4
	Hot wire ignition	1.5mm	UL 746	PLC 4
	Hot wire ignition	Hot wire ignition	3.0mm	UL 746	PLC 4
High voltage arc tracing rate	HVTR	UL 746	PLC 1
Volume resistivity	3.00mm	IEC 60093	1E+14	ohms·cm
Dielectric strength	1.00mm	IEC 60243	24	KV/mm
Arc resistance	3.00mm	ASTM D495	PLC 5
Compared to the anti leakage trace index	3.00mm	IEC 60112	PLC 0
High arc combustion index	0.75mm	UL 746	PLC 0
	High arc combustion index	1.5mm	UL 746	PLC 0
	High arc combustion index	High arc combustion index	3.0mm	UL 746	PLC 0

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.