PLA L175 TOTAL THAILAND

Form：Granules | Grade：Injection grade

Properties:

Biodegradation

Typical Applications:

3D printing materialsFood containersFood Packaging ApplicationsDisposable tableware

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	3D printing materials \| Food containers \| Food Packaging Applications \| Disposable tableware
Properties:	Biodegradation

Certificates

No Data...

Technical Data Sheet

squeeze out	Test Condition	Test Method	Test Result	Test Unit
drying temperature			100	°C
drying time			4.0 to 6.0	hr
Suggested maximum moisture content			0.025	%
Material barrel temperature			20 to 40	°C
Temperature in Zone 1 of the material cylinder			180 to 190	°C
Temperature in Zone 2 of the material cylinder			190 to 210	°C
Oral mold temperature			190 to 210	°C
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus		ISO 527-2	3500	Mpa
tensile strength		ISO 527-2	50.0	Mpa
Tensile strain	Break	ISO 527-2	< 5.0	%
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45 MPa, Unannealed3	ISO 75-2/Bf	55.0 to 60.0	°C
Hot deformation temperature	Hot deformation temperature	0.45 MPa, Unannealed4	ISO 75-2/Bf	100 to 110	°C
Glass transition temperature		DSC	55.0 to 60.0	°C
Melting temperature		DSC	175	°C
Monomer Residue		Internal Method	< 0.30	%
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	190°C/2.16 kg	ISO 1133	3.0	g/10 min
melt mass-flow rate	melt mass-flow rate	210°C/2.16 kg	ISO 1133	8.0	g/10 min
water content		Karl Fisher	< 400	ppm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.