Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.56 g/cm³ |
| Shrinkage rate | | ASTM D955 | 0.27 % |
| Shrinkage rate | | ASTM D955 | 1.2 % |
| Water absorption rate | | ASTM D570 | 0.020 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | M-Scale | ASTM D785 | 100 |
| Rockwell hardness | R-Scale | ASTM D785 | 121 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| bending strength | | ASTM D790 | 235 MPa |
| compressive strength | | ASTM D695 | 190 MPa |
| coefficient of friction | | ASTM D1894 | 0.35 |
| Tensile modulus | | ASTM D638 | 11000 MPa |
| tensile strength | | ASTM D638 | 155 MPa |
| elongation | Break | ASTM D638 | 1.6 % |
| Flexural modulus | | ASTM D790 | 10000 MPa |
| coefficient of friction | | ASTM D1894 | 0.35 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 90 J/m |
| Suspended wall beam without notch impact strength | | ASTM D256 | 450 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| arc resistance | | ASTM D495 | 120 sec |
| Compared to the Leakage Tracking Index (CTI) | | UL 746 | PLC 4 |
| dielectric constant | | ASTM D150 | 4.00 |
| Dissipation Factor | | ASTM D150 | 2E-03 |
| Volume resistivity | | ASTM D257 | 1E+16 ohms·cm |
| dielectric strength | | ASTM D149 | 16 kV/mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 265 °C |
| Linear coefficient of thermal expansion | | ASTM D696 | 2.2E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare