PC 1303AH-15 LG CHEM KOREA

Form：Granules | Grade：UV resistant grade

Properties:

High impact resistanceheat-resisting

Typical Applications:

electrical equipmentLighting applications

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	electrical equipment \| Lighting applications
Properties:	High impact resistance \| heat-resisting

Certificates

No Data...

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result	Test Unit
Refractive index		ASTM D542	1.586
transmissivity		ASTM D1003	89.0	%
turbidity		ASTM D1003	0.70to1.5	%
impact performance	Test Condition	Test Method	Test Result	Test Unit
Dart impact	23°C,3.20mm,TotalEnergy	ASTM D3763	87.0	J
Suspended wall beam without notch impact strength	23°C	ASTM D256	无断裂
Impact strength of cantilever beam gap	23°C,3.20mm	ASTM D256	850	J/m
flammability	Test Condition	Test Method	Test Result	Test Unit
Hot filament ignition temperature	2.0mm	IEC 60695-2-13	850	°C
Extreme Oxygen Index		ASTM D2863	26	%
Average degree of combustion		ASTM D635	3	CM
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus		ASTM D638	2340	Mpa
Wear resistance	雾度变化	Kg/m	45	%
bending strength		ASTM D790	96.0	Mpa
Bending modulus		ASTM D790	2410	Mpa
elongation	Break	ASTM D638	150	%
elongation	elongation	Yield	ASTM D638	6.0	%
tensile strength	Break	ASTM D638	71.0	Mpa
tensile strength	tensile strength	Yield	ASTM D638	60.0	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	MD：-40to82°C	ASTM D696	6.8E-05	cm/cm/°C
Ball pressure temperature		IEC 60598-1	>125	°C
Vicat softening temperature		ASTM D15256	148	°C
Hot deformation temperature	1.8MPa,Annealed,4.00mm	ASTM D648	140	°C
	Hot deformation temperature	1.8MPa,Unannealed,4.00mm	ASTM D648	127	°C
	Hot deformation temperature	Hot deformation temperature	0.45MPa,Annealed,4.00mm	ASTM D648	143	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Equilibrium,23°C,50%RH	ASTM D570	0.32	%
Water absorption rate	Water absorption rate	23°C,24hr	ASTM D570	0.15	%
Shrinkage rate	MD	ASTM D955	0.50-0.70	%
melt mass-flow rate	300°C/1.2kg	ASTM D1238	15	g/10min
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Dielectric strength		ASTM D149	17	KV/mm
Dielectric constant	60Hz	ASTM D150	3.00
Dissipation factor	60Hz	ASTM D150	1E-03
Volume resistivity	23°C	ASTM D257	2E+17	ohms·cm
Compared to the anti leakage trace index	2.00mm	IEC 60112		V
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Scale	ASTM D785	118
Rockwell hardness	Rockwell hardness	M-Scale	ASTM D785	72

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.