PP 7684KN EXXONMOBIL SINGAPORE

Form：Granules | Grade：Impact resistant grade

Properties:

High crystallinityHigh rigidityHigh impact resistanceAntistatic

Typical Applications:

ToolboxIndustrial applicationsTool/parts boxConsumer product application fieldchipLoading boxElectrical appliances

Supplier(1)

Product Description

Certificates(1)

Datasheet

Alternative(1)

Product Description

Typical Applications:	Toolbox \| Industrial applications \| Tool/parts box \| Consumer product application field \| chip \| Loading box \| Electrical appliances
Properties:	High crystallinity \| High rigidity \| High impact resistance \| Antistatic

Certificates

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of cantilever beam gap	-40°C	ISO 180/1A	4.0	kJ/m²
	Impact strength of cantilever beam gap	-18°C	ISO 180/1A	4.6	kJ/m²
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	8.4	kJ/m²
Gardner Impact	-29°C,3.18mm	ASTM D5420	22.7	J
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	3.9	kJ/m²
	Charpy Notched Impact Strength	-20°C	ISO 179/1eA	4.8	kJ/m²
		Charpy Notched Impact Strength	0°C	ISO 179/1eA	6.6	kJ/m²
		Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	10	kJ/m²
Impact strength of cantilever beam gap	23°C	ASTM D256A	150	J/m
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus		ISO 527-2/1	1320	Mpa
tensile strength	Yield	ASTM D638	24.4	Mpa
tensile strength	tensile strength	Yield	ISO 527-2/50	24.3	Mpa
elongation	Yield	ASTM D638	4.4	%
Tensile strain	Yield	ISO 527-2/50	3.4	%
Bending modulus	--3，1%Secant	ASTM D790A	1290	Mpa
	Bending modulus	--4，1%Secant	ASTM D790B	1480	Mpa
	Bending modulus	Bending modulus		ISO 178	1250	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45MPa,Unannealed	ASTM D648	105	°C
	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/Bf	93.0	°C
	Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	51.5	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	230°C/2.16kg	ASTM D1238	20	g/10min

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.