Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.78 g/cm³ |
| Apparent density | | ASTM D1895 | 0.55 g/cm³ |
| Shrinkage rate | | ASTM D955 | 0.10 % |
| Water absorption rate | | ASTM D570 | 0.080 % |
| Water absorption rate | | ASTM D570 | 0.25 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTM D785 | 80 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-1 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTM D638 | 55.0 MPa |
| Flexural modulus | | ASTM D790 | 15900 MPa |
| bending strength | | ASTM D790 | 103 MPa |
| compressive strength | | ASTM D695 | 190 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256A | 54 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric strength | | ASTM D149 | 14 kV/mm |
| dielectric strength | | ASTM D149 | 12 kV/mm |
| arc resistance | | ASTM D495 | 185 sec |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648A | 180 °C |
| Heat distortion temperature | | ASTM D648A | >282 °C |
| Linear coefficient of thermal expansion | | ASTME831 | 2E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | | ASTME831 | 3.9E-05 cm/cm/°C |
| thermal conductivity | | ASTMC518 | 0.79 W/m/K |
| RTI Elec | | UL 746 | 150 °C |
| RTI Imp | | UL 746 | 150 °C |
| RTI | | UL 746 | 150 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare