Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.20 g/cm³ |
| melt mass-flow rate | | ASTM D1238 | 7.0 g/10min |
| Shrinkage rate | | ASTM D955 | 0.50to0.70 % |
| Water absorption rate | | ASTM D570 | 0.15 % |
| Water absorption rate | | ASTM D570 | 0.32 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTM D785 | 74 |
| Rockwell hardness | R-Scale | ASTM D785 | 118 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| Haze ratio | | ASTM D1003 | 0.70to1.5 % |
| refractive index | | ASTM D542 | 1.586 |
| transmissivity | | ASTM D1003 | 89.0 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Limiting Oxygen Index | | ASTM D2863 | 26 % |
| Average degree of combustion | | ASTM D635 | 3 cm |
| UL flame retardant rating | | UL 94 | V-2 |
| UL flame retardant rating | | UL 94 | V-2 |
| UL flame retardant rating | | UL 94 | V-2 |
| UL flame retardant rating | | UL 94 | V-2 |
| GWIT | | IEC 60695-2-13 | 850 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTM D638 | 2410 MPa |
| tensile strength | Yield | ASTM D638 | 60.0 MPa |
| tensile strength | Break | ASTM D638 | 72.0 MPa |
| elongation | Yield | ASTM D638 | 6.0 % |
| elongation | Break | ASTM D638 | 150 % |
| Flexural modulus | | ASTM D790 | 2410 MPa |
| bending strength | | ASTM D790 | 96.0 MPa |
| wear resistance | | ASTM D1004 | 45 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 90 J/m |
| Impact strength of cantilever beam gap | | ASTM D256 | NoBreak |
| InstrumentedDartImpact | | ASTM D3763 | 90.0 J |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ASTM D257 | 2E+17 ohms·cm |
| dielectric strength | | ASTM D149 | 17 kV/mm |
| dielectric constant | | ASTM D150 | 3.00 |
| Dissipation Factor | | ASTM D150 | 1E-03 |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 2 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 145 °C |
| Heat distortion temperature | | ASTM D648 | 129 °C |
| Heat distortion temperature | | ASTM D648 | 142 °C |
| vicat | | ASTM D15255 | 151 °C |
| Ball pressure temperature | | IEC 60598-1 | >125 °C |
| Linear coefficient of thermal expansion | | ASTM D696 | 6.8E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare