Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.27 g/cm³ |
| Shrinkage rate | | ASTMD955 | 0.10到0.40 % |
| Water absorption rate | | ISO62 | 0.30 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | ISO2039-2 | 117 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTMD256 | 100 J/m |
| Charpy Notched Impact Strength | | ISO179/1eA | 8.0 kJ/m² |
| Charpy Notched Impact Strength | | ISO179/1eA | 10 kJ/m² |
| Impact strength of cantilever beam gap | | ASTMD256 | 40 J/m |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile stress | Yield | ISO527-2 | 100 MPa |
| Flexural modulus | | ISO178 | 8800 MPa |
| Bending stress | | ISO178 | 150 MPa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| vicat | | ISO306/B50 | 104 °C |
| | ISO11359-2 | 3E-05 cm/cm/°C |
| | ISO11359-2 | 8E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | | ISO11359-2 | 95 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.