Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.11 g/cm³ |
| Melt volume flow rate | | ISO 1133 | 13.0 cm3/10min |
| Shrinkage rate | | ISO 294-4 | 0.20-0.40 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ISO 2039-2 | 115 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Basic performance | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | | 13 g/10min |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | | 7 KJ/m |
| Flexural modulus | | | 4200 Mpa |
| Tensile modulus | | ISO 527-2 | 4800 Mpa |
| tensile strength | | ISO 527-2 | 83.0 Mpa |
| Flexural modulus | | ISO 178 | 4200 Mpa |
| bending strength | | ISO 178 | 116 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179 | 3.0 kJ/m² |
| Charpy Notched Impact Strength | | ISO 179 | 7.0 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | | 98 °C |
| UL flame retardant rating | | UL 94 | HB |
| Heat distortion temperature | | ISO 75-2/Af | 98.0 °C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 5E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.