Technical Data Sheet
| optical performance | Test Condition | Test Method | Test Result |
|---|
| gloss | | ASTM D-2457 | 87 |
| Haze ratio | | ASTM D-1003 | 10 % |
| other | Test Condition | Test Method | Test Result |
|---|
| characteristic | | | 高抗拉强度和良好的穿刺性、机械加工性能 |
| purpose | | | 重型运输袋、冰袋.冷冻食品袋、马铃薯农用薄膜 |
| Basic performance | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ASTM D-1238 | 0.5 g/10min |
| density | | ASTM D-792 | 0.918 g/cm³ |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTM D-882 | 13 Mpa |
| tensile strength | | ASTM D-882 | 11 Mpa |
| tensile strength | | ASTM D-882 | 43 Mpa |
| tensile strength | | ASTM D-882 | 32 Mpa |
| elongation at break | | ASTM D-882 | 700 % |
| elongation at break | | ASTM D-882 | 850 % |
| Secant modulus | | ASTM D-882 | 220 Mpa |
| Secant modulus | | ASTM D-882 | 260 Mpa |
| Dart impact | | ASTM D-1709 | 200 g |
| Impact strength of cantilever beam gap | | ASTM D256/ISO 179 | 200 kg·cm/cm(J/M)ft·lb/in |
| tensile strength | | ASTM D638/ISO 527 | 43 kg/cm²(MPa)[Lb/in²] |
| elongation | | ASTM D638/ISO 527 | 700 % |
| elongation at break | | ASTM D638/ISO 527 | 850 % |
| Other performance | Test Condition | Test Method | Test Result |
|---|
| Puncture Resistance | | SABIC method | 89 J/mm |
| Elmendorf tear strength | | ASTM D-1922 | 135 g |
| Elmendorf tear strength | | ASTM D-1922 | 400 g |
| Physical properties | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792/ISO 1183 | 0.918 |
| melt mass-flow rate | | ASTM D1238/ISO 1133 | 0.5 g/10min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare