Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ISO1133 | 44 g/10min |
| Shrinkage rate | | ASTMD955 | 0.40to0.60 % |
| Water absorption rate | | ASTMD570 | 0.30 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTMD785 | 115 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO527-2/1 | 2900 Mpa |
| tensile strength | | ASTMD638 | 49.0 Mpa |
| Tensile stress | | ISO527-2/50 | 55.0 Mpa |
| elongation | | ASTMD638 | 15 % |
| Tensile strain | | ISO527-2/50 | >10 % |
| Flexural modulus | | ASTMD790 | 2480 Mpa |
| | ASTMD790 | 77.0 Mpa |
| Bending stress | | ISO178 | 83.0 Mpa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Dissipation Factor | | ASTMD150 | 6.3E-03 |
| Surface resistivity 5 | | ASTMD257 | >1.0E+16 ohms |
| Volume resistivity | | ASTMD257 | >1.0E+16 ohms·cm |
| Dielectric strength 6 | | ASTMD149 | 24 KV/mm |
| dielectric constant | | ASTMD150 | 3.10 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ASTMD648 | 87.0 °C |
| | ASTMD648 | 92.0 °C |
| | ISO75-2/A | 83.0 °C |
| | ASTMD696 | 7E-05 cm/cm/°C |
| thermal conductivity | | ASTMC177 | 0.15 W/m/K |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.