Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.20 g/cm³ |
| melt mass-flow rate | | ASTM D1238 | 14 g/10min |
| Shrinkage rate | | ASTM D955 | 0.0to3.0 % |
| Shrinkage rate | | ASTM D955 | 1.2 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | Shore A | ASTM D2240 | 91 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTM D638 | 7.99 MPa |
| tensile strength | | ASTM D638 | 11.1 MPa |
| tensile strength | | ASTM D638 | 36.9 MPa |
| elongation | Break | ASTM D638 | 410 % |
| Flexural modulus | | ASTM D790 | 41.6 MPa |
| bending strength | | ASTM D790 | 1.90 MPa |
| Taber abraser | | ASTM D1044 | 9.10 mg |
| tensile strength | Ultimate | ASTM D638 | 55.1 MPa |
| elastomer | Test Condition | Test Method | Test Result |
|---|
| tear strength | | ASTM D624 | 96.3 kN/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric strength | | ASTM D149 | 19 kV/mm |
| dielectric constant | | ASTM D150 | 4.80 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| vicat | | ASTM D1525 | 88.0 °C |
| Linear coefficient of thermal expansion | | ASTME831 | 1.6E-04 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.