PA66 PA63R V0 NILIT SUZHOU

Form：Granules | Grade：Injection grade

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Certificates

No Data...

Technical Data Sheet

other	Test Condition	Test Method	Test Result	Test Unit
remarks			阻燃尼龙
characteristic			无卤\磷含量低(-无)
Color			本色
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Impact strength of cantilever beam gap		ASTM D256/ISO 179	4.0	kg·cm/cm(J/M)ft·lb/in
	Impact strength of cantilever beam gap		ASTM D256/ISO 179	3.0	kg·cm/cm(J/M)ft·lb/in
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap		ASTM D256/ISO 179	无断裂	kg·cm/cm(J/M)ft·lb/in
Elongation at Break		ASTM D638/ISO 527	85.0	%
Tensile modulus		ASTM D638/ISO 527	3600	kg/cm²(MPa)[Lb/in²]
tensile strength		ASTM D638/ISO 527	3600	kg/cm²(MPa)[Lb/in²]
elongation		ASTM D638/ISO 527	12	%
Bending modulus		ASTM D790/ISO 178	3600	kg·cm/cm(J/M)ft·lb/in
Elongation at Break		ASTM D638/ISO 527	12	%
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Combustibility (rate)		UL 94	V-0
Hot deformation temperature	HDT	ASTM D648/ISO 75	125-165	℃（℉）
Hot deformation temperature	Hot deformation temperature	HDT	ASTM D648/ISO 75	85-185	℃（℉）
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ASTM D792/ISO 1183	1.14
Shrinkage rate		ASTM D955	18	%
melt mass-flow rate		ASTM D1238/ISO 1133	1.4	g/10min
Water absorption rate		ASTM D570/ISO 62	6.0	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Surface resistivity		ASTM D257/IEC 60093	1.0E+13 OHM	Ω
Arc resistance		ASTM D495/IEC 60112	23
Volume resistivity		ASTM D257/IEC 60093	1.0E+15OHM.CM	Ω.cm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.