Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTMD1505 | <1.45 g/cm³ |
| density | | ASTMD1505 | <1.45 g/cm³ |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore A | ASTMD2240 | <80 |
| Shore A | ASTMD2240 | <80 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Limiting Oxygen Index | | ASTMD2863 | >30 % |
| Limiting Oxygen Index | | ASTMD2863 | >30 % |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| WeightLossonHeating | | | <23 g/m² |
| WeightLossonHeating | | | <23 g/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTMD638 | >15.0 MPa |
| elongation | Break | ASTMD638 | >180 % |
| elongation | | ASTMD638 | >310 % |
| tensile strength | | ASTMD638 | >15.0 MPa |
| elongation | Break | ASTMD638 | >180 % |
| elongation | | ASTMD638 | >310 % |
| aging | Test Condition | Test Method | Test Result |
|---|
| Change rate of tensile strength | | ASTMD471 | <20 % |
| Change rate of ultimate elongation | | ASTMD471 | <20 % |
| Change rate of tensile strength | | ASTMD471 | <20 % |
| Change rate of ultimate elongation | | ASTMD471 | <20 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ASTMD257 | >1.0E+10 ohms·cm |
| dielectric strength | | ASTMD149 | >18 kV/mm |
| Volume resistivity | | ASTMD257 | >1.0E+10 ohms·cm |
| dielectric strength | | ASTMD149 | >18 kV/mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| thermal stability | | | >50 min |
| LowTemperatureBritleness | | | -20 °C |
| thermal deformation | | | <50 % |
| thermal stability | | | >50 min |
| LowTemperatureBritleness | | | -20 °C |
| thermal deformation | | | <50 % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.