PC/ABS MC1300-100 SABIC INNOVATIVE KOREA

Form：Granules | Grade：Injection grade

Properties:

High impact resistanceHigh mobilityEasy electroplating

Typical Applications:

Automotive sector

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Automotive sector
Properties:	High impact resistance \| High mobility \| Easy electroplating

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Dart impact	23°C, Total Energy	ASTM D3763	40.0	J
Dart impact	Dart impact	-30°C, Total Energy	ASTM D3763	33.0	J
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength	Yield, 50.0 mm Span	ASTM D790	72.0	Mpa
Bending modulus	50.0 mm Span	ASTM D790	2060	Mpa
elongation	Break	ASTM D638	150	%
elongation	elongation	Yield	ASTM D638	8.6	%
tensile strength	Break	ASTM D638	44.0	Mpa
tensile strength	tensile strength	Yield	ASTM D638	50.0	Mpa
Tensile modulus		ASTM D638	2130	Mpa
injection	Test Condition	Test Method	Test Result	Test Unit
Temperature in the middle of the barrel			255 to 290	°C
Temperature at the front of the material cylinder			255 to 290	°C
Temperature at the rear of the barrel			250 to 280	°C
Suggested injection volume			30 to 80	%
Suggested maximum moisture content			0.020	%
drying time			3.0 to 4.0	hr
drying temperature			100 to 105	°C
Spray nozzle temperature			260 to 290	°C
Processing (melt) temperature			260 to 290	°C
Mold temperature			75 to 100	°C
Back pressure			0.300 to 0.700	Mpa
Screw speed			40 to 70	rpm
Exhaust hole depth			0.038 to 0.076	mm
thermal performance	Test Condition	Test Method	Test Result	Test Unit
thermal conductivity		ASTM C177	0.20	W/m/K
Linear coefficient of thermal expansion	Across Flow : -40 to 40°C	ASTM E831	9.0E-5	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Flow : -40 to 40°C	ASTM E831	7.2E-5	cm/cm/°C
Vicat softening temperature		ASTM D15255	111	°C
Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	98.0	°C
Hot deformation temperature	Hot deformation temperature	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	115	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	24 hr	ASTM D570	0.10	%
Shrinkage rate	Across FlowFlow : 3.20 mm	Internal Method	0.50 - 0.70	%
Shrinkage rate	Shrinkage rate	Flow : 3.20 mm	Internal Method	0.50 - 0.80	%
melt mass-flow rate	260°C/5.0 kg	ASTM D1238	14	g/10 min

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.